Tooling

Fast Cast Urethane

230-05

Fast Cast Polyurethane

Mix Ratio
100:13
Shore Hardness
82D
Pot Life/Gel Time
15
Compressive Strength (psi)
7300
CTE (in/in/’C)
3.2E-5
Flexural Strength (psi)
3800
Flexural Modulus (psi)
278000
Mixed Viscosity
9000
Shrinkage Percent
nil
Tensile Strength (psi)
1400

Epoxy Surface Coat

500-01

General Purpose Surface Coat - Slow

Mix Ratio
100:16
Shore Hardness
87D
Pot Life/Gel Time
25
Compressive Strength (psi)
11700
CTE (in/in/’C)
2.4E-5
Flexural Strength (psi)
7277
Flexural Modulus (psi)
155950
Mixed Viscosity
40000
Shrinkage Percent
0.00116
Tensile Strength (psi)
2588
500-03

General Purpose Surface Coat - Fast

Mix Ratio
100:23
Shore Hardness
87D
Pot Life/Gel Time
25
Compressive Strength (psi)
14900
CTE (in/in/’C)
1.15E-5
Flexural Strength (psi)
7300
Flexural Modulus (psi)
780000
Mixed Viscosity
40000
Shrinkage Percent
0.00124
Tensile Strength (psi)
2500
502-01

Plastic Faced Plaster Surface Coat

Mix Ratio
100:17
Shore Hardness
86D
Pot Life/Gel Time
42
Compressive Strength (psi)
12300
CTE (in/in/’C)
3.5E-5
Flexural Strength (psi)
6355
Flexural Modulus (psi)
122598
Mixed Viscosity
100000
Shrinkage Percent
nil
Tensile Strength (psi)
3503
 
 
Filled
503-01

Aluminum Filled Surface Coat

Mix Ratio
100:11
Shore Hardness
86D
Pot Life/Gel Time
55
Compressive Strength (psi)
11000
CTE (in/in/’C)
1.13E-5
Flexural Strength (psi)
2000
Flexural Modulus (psi)
150000
Mixed Viscosity
164000
Shrinkage Percent
0.0428
Tensile Strength (psi)
6500
 
 
Filled
504-01

Abrasion Resistant Surface Coat

Mix Ratio
100:10
Shore Hardness
86D
Pot Life/Gel Time
36
Compressive Strength (psi)
11700
CTE (in/in/’C)
2.20E-5
Flexural Strength (psi)
6456
Flexural Modulus (psi)
130000
Mixed Viscosity
33800
Shrinkage Percent
0.00037
Tensile Strength (psi)
3503
 
 
Filled
600-01

Black Polishable Surface - Fast

Mix Ratio
100:18
Shore Hardness
86D
Pot Life/Gel Time
30
Compressive Strength (psi)
15300
CTE (in/in/’C)
4.2E-5
Flexural Strength (psi)
14000
Flexural Modulus (psi)
480000
Mixed Viscosity
50000
Shrinkage Percent
0.00144
Tensile Strength (psi)
5400
 
 
Filled
600-02

Black Polishable Surface - Slow

Mix Ratio
100:19
Shore Hardness
80D
Pot Life/Gel Time
60
Compressive Strength (psi)
15300
CTE (in/in/’C)
4.2E-5
Flexural Strength (psi)
14000
Flexural Modulus (psi)
480000
Mixed Viscosity
50000
Shrinkage Percent
nil
Tensile Strength (psi)
5400
 
 
Filled
603-03

Aluminum Filled Surface Coat - Slow

Mix Ratio
100:11
Shore Hardness
86D
Pot Life/Gel Time
57
Compressive Strength (psi)
11300
CTE (in/in/’C)
2.1E-5
Flexural Strength (psi)
10980
Flexural Modulus (psi)
136929
Mixed Viscosity
56000
Shrinkage Percent
nil
Tensile Strength (psi)
4089
 
 
Filled
603-04

Aluminum Filled Surface Coat - Fast

Mix Ratio
100:13
Shore Hardness
86D
Pot Life/Gel Time
35
Compressive Strength (psi)
12000
CTE (in/in/’C)
2.5E-5
Flexural Strength (psi)
12000
Flexural Modulus (psi)
135000
Mixed Viscosity
52000
Shrinkage Percent
nil
Tensile Strength (psi)
4089
 
 
Filled
604-01

Styrene & Abrasion Resistant Surface Coat

Mix Ratio
100:15
Shore Hardness
86D
Pot Life/Gel Time
35
Compressive Strength (psi)
14300
CTE (in/in/’C)
1.0E-5
Flexural Strength (psi)
6500
Flexural Modulus (psi)
664000
Mixed Viscosity
164000
Shrinkage Percent
0.0002
Tensile Strength (psi)
5400
 
 
Filled

Epoxy Laminating

510-01

General Purpose Laminating

Mix Ratio
100:16
Shore Hardness
86D
Pot Life/Gel Time
25
Compressive Strength (psi)
12900
CTE (in/in/’C)
2.0E-5
Flexural Strength (psi)
9048
Flexural Modulus (psi)
137218
Mixed Viscosity
4500
Shrinkage Percent
nil
Tensile Strength (psi)
4126
 
 
Filled
511-01

General Purpose Laminating

Mix Ratio
100:25
Shore Hardness
84D
Pot Life/Gel Time
20
Compressive Strength (psi)
14200
CTE (in/in/’C)
4.4E-5
Flexural Strength (psi)
8054
Flexural Modulus (psi)
100000
Mixed Viscosity
2000
Shrinkage Percent
0.00347
Tensile Strength (psi)
3867
 
 
Unfilled
515-04

Laminating Paste-Fast

Mix Ratio
100:12
Shore Hardness
60D
Pot Life/Gel Time
75
Compressive Strength (psi)
3520
CTE (in/in/’C)
3.2E-5
Flexural Strength (psi)
7500
Flexural Modulus (psi)
276000
Mixed Viscosity
Paste
Shrinkage Percent
nil
Tensile Strength (psi)
2400
 
 
Filled
515-06

Laminating Paste-Slow

Mix Ratio
100:12
Shore Hardness
60D
Pot Life/Gel Time
120
Compressive Strength (psi)
3280
CTE (in/in/’C)
3.2E-5
Flexural Strength (psi)
7100
Flexural Modulus (psi)
46700
Mixed Viscosity
Paste
Shrinkage Percent
nil
Tensile Strength (psi)
2400
 
 
Filled
515-11

Laminating Putty

Mix Ratio
100:14
Shore Hardness
75D
Pot Life/Gel Time
90
Compressive Strength (psi)
 
CTE (in/in/’C)
1.2E-5
Flexural Strength (psi)
 
Flexural Modulus (psi)
 
Mixed Viscosity
Putty
Shrinkage Percent
nil
Tensile Strength (psi)
 
 
 
Filled
610-01

Aluminum Filled Laminating - Fast

Mix Ratio
100:16
Shore Hardness
87D
Pot Life/Gel Time
35
Compressive Strength (psi)
13900
CTE (in/in/’C)
7.8E-5
Flexural Strength (psi)
11064
Flexural Modulus (psi)
109866
Mixed Viscosity
50000
Shrinkage Percent
0.01645
Tensile Strength (psi)
5547
 
 
Filled
610-04

Aluminum Filled Laminating - Slow

Mix Ratio
100:14.5
Shore Hardness
87D
Pot Life/Gel Time
52
Compressive Strength (psi)
13540
CTE (in/in/’C)
7.85E-05
Flexural Strength (psi)
13000
Flexural Modulus (psi)
90800
Mixed Viscosity
45000
Shrinkage Percent
0.01645
Tensile Strength (psi)
5700
 
 
Filled
611-01

Clear Laminating - Fast

Mix Ratio
100:19
Shore Hardness
86D
Pot Life/Gel Time
37
Compressive Strength (psi)
4300
CTE (in/in/’C)
6.4E-5
Flexural Strength (psi)
16777
Flexural Modulus (psi)
73455
Mixed Viscosity
1300
Shrinkage Percent
0.00461
Tensile Strength (psi)
5724
 
 
Unfilled
611-03

Clear Laminating - Medium

Mix Ratio
100:20
Shore Hardness
80D
Pot Life/Gel Time
45
Compressive Strength (psi)
4300
CTE (in/in/’C)
6.0E-5
Flexural Strength (psi)
16777
Flexural Modulus (psi)
73455
Mixed Viscosity
1300
Shrinkage Percent
0.00461
Tensile Strength (psi)
5724
 
 
Unfilled
611-04

Clear Laminating - Slow

Mix Ratio
100:19
Shore Hardness
78D
Pot Life/Gel Time
55
Compressive Strength (psi)
4300
CTE (in/in/’C)
6.0E-5
Flexural Strength (psi)
16777
Flexural Modulus (psi)
73455
Mixed Viscosity
1300
Shrinkage Percent
0.00461
Tensile Strength (psi)
5724
 
 
Filled
615-07

Laminating Putty

Mix Ratio
100:10
Shore Hardness
75D
Pot Life/Gel Time
90
Compressive Strength (psi)
 
CTE (in/in/’C)
1.2E-5
Flexural Strength (psi)
 
Flexural Modulus (psi)
 
Mixed Viscosity
Putty
Shrinkage Percent
nil
Tensile Strength (psi)
 
 
 
Filled
615-12

Laminating Putty

Mix Ratio
100:14
Shore Hardness
75D
Pot Life/Gel Time
90
Compressive Strength (psi)
 
CTE (in/in/’C)
1.2E-5
Flexural Strength (psi)
 
Flexural Modulus (psi)
 
Mixed Viscosity
Putty
Shrinkage Percent
nil
Tensile Strength (psi)
 
 
 
Filled

Epoxy Casting

523-01

Aluminum Filled Surface Casting - Fast

Mix Ratio
100:10
Shore Hardness
86D
Pot Life/Gel Time
82
Compressive Strength (psi)
8540
CTE (in/in/’C)
3.7E-5
Flexural Strength (psi)
6398
Flexural Modulus (psi)
91814
Mixed Viscosity
6400
Shrinkage Percent
nil
Tensile Strength (psi)
3366
 
 
Filled
524-01

Abrasion Resistant Surface Coat - Fast

Mix Ratio
100:10
Shore Hardness
87D
Pot Life/Gel Time
63
Compressive Strength (psi)
14000
CTE (in/in/’C)
2.5E-5
Flexural Strength (psi)
6140
Flexural Modulus (psi)
148438
Mixed Viscosity
15400
Shrinkage Percent
0.00251
Tensile Strength (psi)
3879
 
 
Filled
533-01

Aluminum Filled Mass Casting - Slow

Mix Ratio
100:12
Shore Hardness
87D
Pot Life/Gel Time
198
Compressive Strength (psi)
8300
CTE (in/in/’C)
6.8E-5
Flexural Strength (psi)
6870
Flexural Modulus (psi)
95192
Mixed Viscosity
6100
Shrinkage Percent
0.00129
Tensile Strength (psi)
3360
 
 
Filled
534-01

Abrasion Resistant Mass Casting - Slow

Mix Ratio
100:12
Shore Hardness
86D
Pot Life/Gel Time
150
Compressive Strength (psi)
10500
CTE (in/in/’C)
8.1E-5
Flexural Strength (psi)
6100
Flexural Modulus (psi)
440000
Mixed Viscosity
11700
Shrinkage Percent
0.00166
Tensile Strength (psi)
3270
 
 
Filled
623-01

Aluminum Filled Casting - Fast

Mix Ratio
100:7
Shore Hardness
87D
Pot Life/Gel Time
50
Compressive Strength (psi)
12000
CTE (in/in/’C)
2.8E-5
Flexural Strength (psi)
6978
Flexural Modulus (psi)
185114
Mixed Viscosity
24400
Shrinkage Percent
nil
Tensile Strength (psi)
3480
 
 
Filled
633-01

High Thermally Conductive Filled Casting

Mix Ratio
100:9.3
Shore Hardness
80D
Pot Life/Gel Time
100
Compressive Strength (psi)
10000
CTE (in/in/’C)
3.7E-5
Flexural Strength (psi)
6280
Flexural Modulus (psi)
926000
Mixed Viscosity
19000
Shrinkage Percent
nil
Tensile Strength (psi)
3240
 
 
Filled
633-02

High Thermally Conductive Filled Casting

Mix Ratio
100:9.3
Shore Hardness
 
Pot Life/Gel Time
64
Compressive Strength (psi)
10000
CTE (in/in/’C)
3.2E-5
Flexural Strength (psi)
6280
Flexural Modulus (psi)
926000
Mixed Viscosity
22000
Shrinkage Percent
nil
Tensile Strength (psi)
3240
 
 
Filled

Tooling Board

E-65

Epoxy Tooling Board - 65 pcf

Shore Hardness
85D
Compressive Strength (psi)
8000
CTE (in/in/’C)
3x10-5
Flexural Strength (psi)
20900
Flexural Modulus (psi)
653000
Shrinkage Percent
N/A
Tensile Strength (psi)
7000
 
Filled
E-90

Epoxy Tooling Board - 90 pcf

Shore Hardness
85D
Compressive Strength (psi)
8000
CTE (in/in/’C)
3x10-5
Flexural Strength (psi)
20900
Flexural Modulus (psi)
653000
Shrinkage Percent
N/A
Tensile Strength (psi)
7000
 
Filled

Urethane Potting

720-01A

Shore 20 A Urethane - Slow

Mix Ratio
100:120
Shore Hardness
 20A
Pot Life/Gel Time
10
CTE (in/in/’C)
2.44E-5
Mixed Viscosity
1800
Shrinkage Percent
0.0078
Tensile Strength (psi)
162
720-02A

Shore 20A Urethane - Fast

Mix Ratio
100:120
Shore Hardness
 20A
Pot Life/Gel Time
10
CTE (in/in/’C)
2.44E-5
Mixed Viscosity
1800
Shrinkage Percent
0.0078
Tensile Strength (psi)
162
735-01A

Shore 35A Urethane

Mix Ratio
100:27
Shore Hardness
35A
Pot Life/Gel Time
15
CTE (in/in/’C)
9.7E-5
Mixed Viscosity
7000
Shrinkage Percent
0.00249
Tensile Strength (psi)
361
740-01A

Shore 40A Optically Clear Urethane

Mix Ratio
100:98
Shore Hardness
40A
Pot Life/Gel Time
12
CTE (in/in/’C)
4.16E-5
Mixed Viscosity
750
Shrinkage Percent
nil
Tensile Strength (psi)
475
755-01A

Shore 55A Urethane

Mix Ratio
100:27
Shore Hardness
55A
Pot Life/Gel Time
30
CTE (in/in/’C)
2.36E-5
Mixed Viscosity
1000
Shrinkage Percent
0.00571
Tensile Strength (psi)
475
770-01D

High Impact Resistant Urethane

Mix Ratio
100:75
Shore Hardness
70D
Pot Life/Gel Time
30
CTE (in/in/’C)
8.7E-5
Mixed Viscosity
8500
Shrinkage Percent
nil
Tensile Strength (psi)
8470
775-01A

Shore 75A Urethane

Mix Ratio
100:34.1
Shore Hardness
77A
Pot Life/Gel Time
6
CTE (in/in/’C)
1.81E-5
Mixed Viscosity
700
Shrinkage Percent
0.00142
Tensile Strength (psi)
2840

Miscellaneous

810-01

Durable Epoxy Model & Tooling Board

Mix Ratio
100:50
Shore Hardness
70D
Pot Life/Gel Time
17
Compressive Strength (psi)
8000
CTE (in/in/’C)
5x10-5
Flexural Strength (psi)
 
Flexural Modulus (psi)
 
Mixed Viscosity
18000
Shrinkage Percent
nil
Tensile Strength (psi)
6000
811-01

General Purpose Epoxy Adhesive Rapid Cure

Mix Ratio
100:100
Shore Hardness
80D
Pot Life/Gel Time
5
Compressive Strength (psi)
9800
CTE (in/in/’C)
8.6E-5
Flexural Strength (psi)
6100
Flexural Modulus (psi)
200000
Mixed Viscosity
12000
Shrinkage Percent
0.1142
Tensile Strength (psi)
2800
813-01

General Purpose Aluminum Filled Epoxy System

Mix Ratio
100:100
Shore Hardness
80D
Pot Life/Gel Time
30
Compressive Strength (psi)
11400
CTE (in/in/’C)
3.2x10-5
Flexural Strength (psi)
14200
Flexural Modulus (psi)
 
Mixed Viscosity
18000
Shrinkage Percent
nil
Tensile Strength (psi)
6000
 
 
Filled

Order Online

Shop our secure online store.  Can't find what you need? We will custom formulate a product for your unique application without the custom cost.
SHOP ONLINE
linkedin facebook pinterest youtube rss twitter instagram facebook-blank rss-blank linkedin-blank pinterest youtube twitter instagram